怎样正确使用彩涂板

1、 彩涂钢板的螺栓头应用防水材料密封，以防外部影响生锈。
2、 如果由于不同的外部因素导致产品上出现锈斑，应迅速除锈，彩涂钢板并刷涂或喷涂同一颜色的涂层。

3、 按照设计要求，彩涂钢板由于各厂家的产品不尽相同，为了保证工作的顺利完成，我们应该采用同一家公司、统一规格的产品。
4、 在吊装和运输过程中，应防止漆膜损伤、表面污染和碰撞。
5、 在储存、运输和使用过程中，应远离酸、碱、盐、有机溶剂等腐蚀性物质，防止雨淋和冷凝，不得浸泡或沾污。
6、 在运输过程中，应使用薄膜将各层隔开，以避免相对滑动和磨损。
7、 彩涂钢板加工的环境温度应在7℃以上；加工辊系的间隙应根据板材厚度进行调整，并清除辊面和支承板上的异物；同时，检查板材两侧油漆是否脱落。如有脱漆现象，应查明原因并采取措施后方可加工。
8、 应在正常气候条件下使用，作为屋面产品，坡度不应小于10度。
9、 严禁用切割机切割彩涂钢板，以免切割产生的高温金属粉末粘在产品上生锈。

1、 The bolt head of color coated steel plate shall be sealed with waterproof material to prevent rust caused by external influence.

2、 If rust spots appear on the product due to different external factors, the rust shall be removed quickly and the coating of the same color shall be brushed or sprayed.
3、 According to the design requirements, because the products of all manufacturers are not the same, in order to ensure the smooth completion of the work, we should use the same company, unified specifications of products.
4、 In the process of hoisting and transportation, it is necessary to prevent film damage, surface pollution and collision.
5、 In the process of storage, transportation and use, keep away from acid, alkali, salt, organic solvent and other corrosive substances; prevent rain and condensation, and do not immerse or get muddy.
6、 During transportation, the layers should be separated by thin films to avoid relative sliding and abrasion.
7、 The ambient temperature of color coated steel plate processing should be above 7 ℃; the gap of processing roller system should be adjusted according to the thickness of the plate, and the foreign matters on the roller surface and supporting plate should be removed; at the same time, whether the paint is removed on both sides of the plate should be checked. If the paint is removed, the reason should be found out and measures should be taken before processing.
8、 It should be used under normal climatic conditions, as a roofing product, the slope should not be less than 10 degrees.
9、 It is strictly forbidden to use the cutting machine to cut the color coated steel plate, so as to avoid the high temperature metal powder generated by cutting from sticking to the product and rusting.